TYPE

USES AND APPLICATIONS

ALLOY FOR RECONSTRUCTIONS ON CARBON STEEL TO WITHSTAND HIGH IMPACT AND LIGHT ABRASION. TO CLAD TRACTOR SPROCKETS, ROLLERS, ROLLING MILLS, ETC. AND TO PREPARE THE SURFACE FOR EVEN HARDER CLADDING ON CARBON STEEL. Rc HARDNESS- FIRST WELD BEAD: 20' TO 25, SECOND WELD BEAD: 25 TO 35.

WELDING ROD WITH LOW HYDROGEN CONTENT COVERING MADE WITH CHROMIUM, MANGANESE, MOLYBDENUM AND CARBON. IT IS ABLE TO WITHSTAND EXTREME ABRASION AND MODERATE IMPACT. Rc HARDNESS-  FIRST WELD BEAD:45-50, SECOND WELD BEAD: 50-55.

TO CLAD AUSTENITIC MANGANESE   STEEL PARTS. FILLER METAL DEPOSITS HARDEN AS THEY COOL DOWN WITH THE SURROUNDING AIR. ABRASION AND IMPACT RESISTANCE EQUALS THAT OF HEAT TREATED MANGANESE STEEL. FILLER METAL DEPOSITS HARDEN WITH IMPACT AND ACHIEVE OUTSTANDING RESISTANCE.

WELDING ROD TO CLAD STEEL SUBMITTED TO EXTREME ABRASION AND MODERATE IMPACT LIKE EXCAVATION MACHINERY PARTS, CONCRETE MIXERS, BUCKETS, DREDGERS, STONE CRUSHING EQUIPMENT, MIXING BLADES, SIEVES, DIRT MOVING EQUIPMENT, MILL PARTS AND ALSO THOSE PARTS SUBMITTED TO ABRASION, HEAT AND CORROSION. HARDNESS: UP TO 58 Rc. .

THIS WELDING ROD FILLER METAL WITHSTANDS INTENSE ABRASION, EROSION AND/OR CAVITATION TOGETHER WITH FRICTION, SEVERE CORROSION AND HEAT. IT IS USED IN THE MINING, CEMENT AND SUGAR INDUSTRIES,  IN STONE MILL  PARTS, EXCAVATOR PARTS, STONE CRUSHING EQUPMENT, CONCRETE MIXERS, DREDGERS, MIXING BLADES, CAT CRAWL BUCKETS, MILL PARTS. HARDNESS: BETWEEN 56 AND 62 Rc.

THIS WELDING ROD IS MADE WITH CHROMIUM CARBIDE TO RECONDITION SUGAR MILL TANDEMS, SUGAR MILL ROLLER TEETH SIDES WITHOUT THE NEED TO STOP OPERATIONS DUE TO DISASSEMBLIG AND REASSEMBLING OF TANDEMS..

WELDING ROD WITH SINTERIZED TUNGSTEN CARBIDE PARTICLES ON A BRONZE NICKEL CORE FOR APPLICATION WITH OXYFUEL GAS TORCH. IT IS IDEAL TO CLAD OIL DRILLING BITS AND IN GENERAL, FOR EXCAVATION EQUIPMENT AND FOR ROTARY TYPE TOOLS USED IN DRILLING OPERATIONS.

ELECTRODE FOR COVERING WORN PARTS OF STEEL TO CARBON, STEEL TO MANGANESE, FORGED IRON OR PARTS THAT ARE SUBJECTED TO WEAR BY ABRASION AND LIGHT IMPACT. HARDNESS: 43-48 HRC

ELECTRODE BASE CHROME, MANGANESE, MOLYBDENUM AND VANADIUM OF HIGH PERFORMANCE, USED TO COVER PARTS SUBJECT TO WEAR BY ABRASION, IMPACT AND COMPRESSION AT TEMPERATURES OF UP TO 550 ° C. HARDNESS: 55-60 HRC.

HARDNESS : 280-320 HB

ELECTRODE FOR COATING PARTS SUBJECTED TO ABRASION BY FRICTION AND LIGHT IMPACT, IN THE CONSTRUCTION INDUSTRY, IN MACHINERY PARTS FOR EXCAVATION AND MOVEMENT OF EARTH AND / OR ROCK, SPOONS OF EXCAVATORS OF DRIVER, ALSO FOR PARTS SUBJECTED TO WEAR IN THE INTERNAL OR EXTERNAL FACES, AS ARE MILLS. GOOD RESISTANCE TO OXIDATION. HARDNESS: 55-60 HRC

TO COVER PARTS THAT ARE SUBJECTED TO WEAR BY SEVERE ABRASION AND MODERATE IMPACT, IN OPERATIONS OF REPAIR OF THE MINING INDUSTRY, CEMENTERY, SUGAR-INGENIOS, EXAMPLE; MACHINERY FOR EXCAVATION, MILLS FOR CRUSHING AND MOLERING ABRASIVE MATERIALS, MIXERS. HARDNESS: 57-62 HRC.